Polyethers containing 4-(carbazol-2-yl)-7-arylbenzo[c]-1,2,5-thiadiazole chromophores as solution processed materials for hole transporting layers of OLEDs

Two polyethers containing electroactive pendent 4-(carbazol-2-yl)-7-arylbenzo[c]-1,2,5-thiadiazole moieties have been synthesized by the multi-step synthetic route. Full characterization of their structures is presented. The polymers represent derivatives of very high thermal stability with initial thermal degradation temperatures of 425 °C and 431 °C. Glass transition temperatures of the amorphous materials were also very high and reached values of 154 °C and 163 °C. The electron photoemission spectra of thin layers of the polymers showed ionization potentials of 5.84 eV and 5.93 eV. Hole-transporting properties of the polymeric materials were tested in the structures of organic light emitting diodes with Alq3 as the green emitter and electron transporting material. An electroluminescent device containing hole-transporting layer (HTL) of the polymer with electroactive 4-carbazolyl-7-phenylbenzo[c]-1,2,5-thiadiazole moieties exhibited turn on voltage of 6.2 V, maximum photometric efficiency of 2.5 cd/A and maximum brightness exceeding 300 cd/m2. The device containing HTL of the polymer with 4-carbazolyl-7-(1-naphtyl)benzo[c]-1,2,5-thiadiazole moieties demonstrated turn on voltage of 5.2 V, maximum photometric efficiency of 1.6 cd/A and maximum brightness exceeding 1500 cd/m2. The efficiencies were about 30-90% higher than that of the device containing widely used hole transporting layers of poly(9-vinylcarbazole).