Precursors of binary alloy (Fe1/2Co1/2, Fe1/2Ni1/2, Ni1/2Co1/2, hereinafter referred to as FeCo, FeNi, NiCo) coated cenospheres were prepared by heterogeneous precipitation under optimized conditions. Magnetic binary alloy coated cenosphere composites with core–shell structure were subsequently obtained by thermal reduction of the as-prepared precursors at 700 °C for 2 h under H2/N2 atmosphere. The results showed that the alloy coatings were uniform and the binary alloy coated cenosphere composites basically retained the spherical morphology, suggesting that the thickness of the alloy coating could be adjusted to fabricate core–shell composites with multilayer structures. The composites exhibited higher coercivity than the pure alloy powders, and could therefore be used for high-performance functional materials and devices.
Magnetic binary alloy coated cenosphere composites, with spherical morphology, core–shell structure and coating grain sizes below 40 nm, were obtained. The composites exhibited higher coercivity than the pure alloy powders.Figure optionsDownload as PowerPoint slide
Journal: Particuology - Volume 10, Issue 3, June 2012, Pages 334–338