Development of a novel gas sensor based on oxide thick films
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
مواد الکترونیکی، نوری و مغناطیسی
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Zinc and iron oxide thick film gas sensors were fabricated using screen-printing technology on glass substrates that had silver interdigitated electrodes. The sensor was used to detect methanol, ethanol and propanol with a concentration range of 0-8000 ppm. Using the formula to calculate a change in resistance, ÎR = Rgas â Rair, resistance was seen to increase linearly alongside increasing concentrations of the gas vapours. The sensor showed the highest sensitivity to propanol followed by ethanol and methanol when the operating temperature was 25 °C. The sensitivities (slope of graphs) of methanol, ethanol and propanol changed from 0.07, 0.5, and 3.54 to 0.075, 0.115, and 0.5 Ω/ppm when the operating temperature was increased from 25 to 50 °C. The response/recovery times of the sensor for 4000 ppm at room temperature were, 10/10, 15/20 and 40/70 s for methanol, ethanol and propanol, respectively. X-ray diffraction (XRD) was used to examine the final composition of the film, while scanning electron microscopy (SEM) was used to examine the final composition of grain size. The final composition has two phases: ZnO and ZnFe2O4
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: B - Volume 118, Issues 1â3, 25 April 2005, Pages 44-49
Journal: Materials Science and Engineering: B - Volume 118, Issues 1â3, 25 April 2005, Pages 44-49
نویسندگان
K. Arshak, I. Gaidan,