Large spot laser assisted GMA brazing-fusion welding of aluminum alloy to galvanized steel
ترجمه فارسی عنوان
لیزر نقطه ای بزرگ کمک جوشکاری به جوشکاری از جنس آلومینیوم به فولاد گالوانیزه
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
جوشکاری فیوژن جوشکاری جوشکاری هیبرید لیزری قوس، مشترک آلومینیوم و فولاد، شکل جوش، ویژگی های مکانیکی،
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی صنعتی و تولید
چکیده انگلیسی
Through positioning the leading laser as an auxiliary role, and the trailing arc as the main heat source, aluminum alloy (Al) was joined to galvanized steel plate with lap joint. The brazed seam width w increased with the increasing of heat input. The appropriate laser-wire distance Dlw and defocusing distance df to obtain the good fusion weld appearance were 5Â mm and +20Â mm, respectively. The fracture position of tensile test sample was divided into brazed interface fracture (PÂ <Â 0.6Â kW) and HAZAl fracture (PÂ >Â 0.6Â kW). The maximum tensile strength of dissimilar joint reached 75% of that of Al. The shear strength was mainly decided by heat input, and the brazed seam had the highest microhardness. Joining mechanism of this process was summarized into two factors: the effective function of laser and the metallurgical function of zinc. Compared to gas metal arc welding (GMAW), large spot laser assisted GMA process improved weld appearance and enhanced the process stability and its time-efficiency.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Materials Processing Technology - Volume 214, Issue 11, November 2014, Pages 2684-2692
Journal: Journal of Materials Processing Technology - Volume 214, Issue 11, November 2014, Pages 2684-2692
نویسندگان
Guoliang Qin, Zhen Lei, Yuhu Su, Banglong Fu, Xiangmeng Meng, Shangyang Lin,