![عکس صفحه اول مقاله: Growth and spectral characteristics of a new promising stoichiometric laser crystal: Ca9Yb(VO4)7 Growth and spectral characteristics of a new promising stoichiometric laser crystal: Ca9Yb(VO4)7](/preview/png/1259110.png)
A Ca9Yb(VO4)7 crystal with dimensions of Φ23 mm×35 mm was grown successfully by Czochralski method. Its thermal conductivity was 1.06 W/(m·K) at room temperature. The absorption cross-sections at 980 nm were 1.80×10−20 cm2 and 1.28×10−20 cm2 for π-and σ-polarizations, respectively, with a full-width at half-maximum of 34 nm. The crystal had a broad emission at around 1025 nm with a full-width at half-maximum of 67 nm for π-polarization and 70 nm for σ-polarization. The emission cross-sections of the crystal were calculated by using reciprocity method and Füchtbauer-Ladenburg formula. The emission cross-sections at 1025 nm were 3.57×10−20 cm−2 and 1.91×10−20 cm−2 for π- and σ-polarization, respectively. The fluorescence lifetime was 332 μs. The results indicated that the crystal is a promising femtosecond and tunable laser material.
Graphical AbstractPolarization absorption and fluorescence spectra of Ca9Yb(VO4)7 crystalFigure optionsDownload as PowerPoint slide
Journal: Journal of Rare Earths - Volume 33, Issue 3, March 2015, Pages 239–243