SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDX), UV-visible spectrophotometer and automatic colorimeter were used to investigate the properties of the samples. The results showed that the compact SiO2 film formed on the surface of Ce2S3 pigment at a cerium silicon molar ratio of 2. The thermal stability temperature of Ce2S3 pigment was improved to 450 °C after SiO2 coating. In addition, the color of Ce2S3 pigment was not affected significantly through coating colorless and transparent SiO2 and it could be used as safe red pigment in higher temperature fields.
SEM image and UV-visible absorption spectrum of Ce2S3 and SiO2 coated Ce2S3 pigmentFigure optionsDownload as PowerPoint slide
Journal: Journal of Rare Earths - Volume 31, Issue 9, September 2013, Pages 891–896