Chiral separation of trans-stilbene oxide through cellulose acetate butyrate membrane

An enantioselective membrane was prepared using cellulose acetate butyrate as a membrane material. The flux and permselective properties of membrane using 50% ethanol solution of (R,S)-trans-stilbene oxide as feed solution were studied. The top surface and cross-section morphology of the resulting membrane were examined by scanning electron microscopy. The resolution of over 92% enantiomeric excess was achieved when the enantioselective membrane was prepared with 15 wt % cellulose acetate butyrate and 30 wt % N,N-dimethylformamide in the casting solution of acetone, 10 °C temperature of water bath for the gelation of the membrane, and the operating pressure and the feed concentration of the trans-stilbene oxide were 3 kgf/cm2 and 5.2 mmol/L, respectively. Since the cellulose acetate butyrate contained a large amount of asymmetric carbons on the backbone structure, it was possible to form helical structure, this was considered to be the reason for the enantioselectivity of the membrane.

Figure optionsDownload as PowerPoint slide