• We analysis influence of cooling rate on obtained microstructure.
• Silicon addition had important influence on phase transformation.
• Proper cooling rate allowed to protect materials against precipitation.
This paper discusses issues related to modifying the structure of material depending on the amount of silicon carbide additive and on the applied cooling rate. The study was conducted for Astaloy CrL modified powder with 1 wt.% or 3 wt.% SiC addition and 0.6% C introduced through mechanical alloying. It was concluded that the MA process as well as the addition of silicon have a significant influence on lowering the temperature of iron alloyed with 1.5 wt.% Cr and 0.2 wt.% Mo transformation. Moreover, changing the cooling rate has a very significant influence on formation and control of the sintered material’s microstructure. It was further observed that silicon carbide decomposes and silicon diffuses into the Astaloy CrL base powder.
Figure optionsDownload as PowerPoint slide
Journal: Advanced Powder Technology - Volume 25, Issue 2, March 2014, Pages 543–550