pH-dependent formation of AACH fibers with tunable diameters and their in situ transformation to alumina nanocrystals with mesoporous structure
موضوعات مرتبط
مهندسی و علوم پایه مهندسی شیمی مهندسی شیمی (عمومی)
پیش نمایش صفحه اول مقاله
pH-dependent formation of AACH fibers with tunable diameters and their in situ transformation to alumina nanocrystals with mesoporous structure
چکیده انگلیسی

Through a simple hydrothermal and thermal decomposition process of the ammonium aluminum carbonate hydroxide (denoted as AACH) precursors, we prepared mesoporous γ-Al2O3 fibers with tunable diameters by manipulating the amount of urea (pH-adjuster) in the reaction mixture (i.e., pH control). The experimental results show that the diameter of the obtained AACH fibers decreased obviously when the pH values of the reaction mixtures changed from 2.5 to 5.0. The as-formed precursors could transform to the morphology-remained cubic γ-Al2O3 with a slight shrinkage in diameter of the fibers after an annealing process. N2 adsorption–desorption experiment indicates that the as-synthesized alumina microfibers and nanofibers have large surface area (176 and 230 m2/g, respectively) and narrow pore-size distributions. Both the γ-Al2O3 microfibers and nanofibers are powerful in the removal of Congo red pollutant from waste water.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Advanced Powder Technology - Volume 23, Issue 2, March 2012, Pages 164–169
نویسندگان
, , , , ,