![عکس صفحه اول مقاله: Microstructure and mechanical properties of alloy C-276 weldments fabricated by continuous and pulsed current gas tungsten arc welding techniques Microstructure and mechanical properties of alloy C-276 weldments fabricated by continuous and pulsed current gas tungsten arc welding techniques](/preview/png/1696990.png)
Effects of switching over from gas tungsten arc welding (GTAW) to pulsed current gas tungsten arc welding (PCGTAW) on the quality of joints produced in Hastelloy C-276 material were investigated. Welding was carried out both by autogenous mode and using ERNiCrMo-3 filler wire. Microstructures of weld joints produced with and without current pulsing were studied using optical and scanning electron microscopy. Microsegregation occurring in GTAW and PCGTAW joints was investigated using energy dispersive X-ray spectroscopy (EDS). Strength and ductility of weld joints produced with and without pulsing were evaluated. The results show that pulsing results in refined microstructure, reduced microsegregation and improved strength of weld joints. Secondary phase(s) noticed in GTA weldments were found to be absent in PCGTA weldments. Autogenous PCGTA weldments were found to be the best in terms of: (i) freedom from microsegregation, (ii) strength and (iii) freedom from unwanted secondary phases.
Journal: Journal of Manufacturing Processes - Volume 16, Issue 4, October 2014, Pages 563–572