Tool wear of coated drills in drilling CFRP

This study aimed to investigate the wear of certain coated drills when drilling carbon fiber reinforced composites (CFRP). Three different drills were used in the drilling experiments: uncoated, diamond coated and AlTiN coated carbide (WC–Co) drills. The tool wear in CFRP machining was quite different from that in conventional metal machining. The primary wear type was a dulling or blunting of the cutting edge, which has been referred to as edge rounding wear or edge recession. In this paper, a hypothesis has been developed to explain the edge rounding wear in CFRP machining. Due to the fracture-based chip formation of CFRP, there is lack of the work material stagnation zone in front of the cutting edge, which normally prevents the edge wear in metal machining. Series of wear lead to rapid dulling of the cutting edge. The resistance to edge rounding wear on the coated as well as uncoated drills has been investigated. The diamond coating significantly reduces the edge rounding wear. However, AlTiN coated drills showed no visible improvement over the uncoated carbide drill, despite of their high hardness, thus not protecting the drill. The wear mechanisms of the uncoated carbide drill and coatings are discussed. It is believed that the 2-body and 3-body abrasive wear fail to explain the observed tool wear in CFRP drilling. However, the wear of the coatings and uncoated carbide substrate from tribo-meter tests correlated well with the tool wear in the CFRP drilling. Therefore, the tribo-meter test can be used to screen the prospective tool materials before carrying drilling experiment.