Effect of excitation wavelength on electron injection efficiency in dye-sensitized nanocrystalline TiO2 and ZrO2 films

The effect of excitation wavelength on the efficiency of electron injection from N3 dye (cis-bis(4,4′-dicarboxy-2,2′-bipyridine)di(thiocyanato)ruthenium(II); Ru(dcbpy)2(NCS)2) to nanocrystalline TiO2 and ZrO2 films was studied by transient absorption spectroscopy. For TiO2 films, electron injection occurred efficiently (> 80 %), and the efficiency did not depend on excitation wavelength. For ZrO2 films, no electron injection was observed even with shorter-wavelength excitation in a polar solvent. To cite this article: R. Katoh et al., C. R. Chimie 9 (2006).

RésuméL’effet de la longueur d’onde d’excitation sur l’efficacité de l’injection d’électrons à partir du pigment N3 (cis-bis(4,4′-dicarboxy-2,2′-bipyridine) di(thiocyanato)ruthénium(II) ; Ru(dcbpy)2(NCS)2) vers des films nanocristallins de TiO2 et de ZrO2 a été étudié par spectroscopie d’absorption transitoire. Pour les films de TiO2, l’injection d’électrons s’est faite avec une bonne efficacité (> 80%), indépendante de la longueur d’onde d’excitation. Pour les films de ZrO2, aucune injection d’électrons n’a été observée, même avec une excitation de longueur d’onde plus courte dans un solvant polaire. Pour citer cet article : R. Katoh et al., C. R. Chimie 9 (2006).