Crystallographic, magnetic and electric studies of a new pyrochlore-like structure (Bi1.56Co0.44)(Sb1.48Co0.52)O7 compound

A new pyrochlore-type structure (Bi1.56Co0.44)(Sb1.48Co0.52)O7 compound has been synthesized using ceramic method in air. Rietveld refinements using X-ray powder diffraction data confirmed an overall A2B2O7 cubic pyrochlore structure with a = 10.44896 (2) Å and Fd-3m symmetry. The reliability factors are Rwp = 3.09%; Rp = 2%; Rexp = 1.39% and RBragg = 4.38%. The magnetic susceptibility measurements achieved between 4 and 800 K indicate a paramagnetic behaviour with an oxidation state “+2” of the cobalt ion. The electric resistivity measured using the complex impedance spectroscopy method evidenced an increase of the electric conductivity with the temperature, which reached 1.88 × 10−3 (ohm cm)−1 at 775 K.

RésuméUn nouveau composé de type pyrochlore, de formule (Bi1,56Co0,44)(Sb1,48Co0,52)O7, a été synthétisé par la méthode céramique à l'air. La résolution structurale par la méthode de Rietveld confirme que le composé pyrochlore de formule A2B2O7 est cubique, de paramètre de maille a = 10,44896 (2) Å et de groupe d'espace Fd-3m. Les facteurs de reliabilité sont Rwp = 3,09% ; Rp = 2% ; Rexp = 1,39% et RBragg = 4,38%. Les mesures magnétiques effectuées entre 4 et 800 K indiquent que le composé est paramagnétique et que le cobalt se trouve à l'état d'oxydation « +2 ». La résistivité électrique mesurée par la méthode d'impédance complexe montre que la conductivité électrique augmente avec la température et donne 1,88 × 10−3 (ohm cm)−1 à 775 K.