Structure and magnetic behaviors of melt-spun SmFeSiB ribbons and their nitrides
موضوعات مرتبط
مهندسی و علوم پایه فیزیک و نجوم فیزیک ماده چگال
پیش نمایش صفحه اول مقاله
Structure and magnetic behaviors of melt-spun SmFeSiB ribbons and their nitrides
چکیده انگلیسی


• Rietveld analysis shows that the augment of Fe content gives rise to an increase of the c/a ratio and cell volume.
• The isomer shift of 2e atom shows a noticeable increase according to Fe content, which corroborates the preferential occupation of excessive Fe atoms at this site.
• The hyperfine fields at various Fe sites follow the order H2e>H3g>H6l, which corresponds closely with the number of iron near neighbor of each site.

SmFe9.3+xSi0.2B0.1 (x=0, 0.5, 1.0) ribbons and their nitrides were prepared by melt-spinning, followed by annealing and subsequent nitriding. The structure and magnetic properties have been investigated by means of powder X-ray diffraction, vibrating sample magnetometer and Mossbauer spectroscopy. Rietveld analysis shows that the augment of Fe content gives rise to an increase of the c/a ratio and cell volume. The increasing amount of Fe atoms occupying the 2e sites results in the change of initial structure. It is indicated that the isomer shift of 3g and 6l atom remains quasi-constant while the 2e atom shows a noticeable increase with the increase of iron content, which further conforms the preferential occupation of excessive Fe atoms at this site. Consistent with Tc, the mean hyperfine field 〈Bhf〉 has the highest value of 25.7 T when x=0.5. The hyperfine fields at different Fe sites follow the order H2e>H3g>H6l. The highest curie temperature of 477.68 K and the hyperfine field of 25.7 T in the as-quenched ribbons were obtained when x=0.5. Meanwhile, the highest magnetic properties of Hcj=4.31 kOe, (BH)m=3.5 MGOe in the nitride powders were found.