![عکس صفحه اول مقاله: Magnetocaloric properties of LaFe13−x−yCoxSiy and commercial grade Gd Magnetocaloric properties of LaFe13−x−yCoxSiy and commercial grade Gd](/preview/png/1801241.png)
The magnetocaloric properties of three samples of LaFe13−x−yCoxSiy have been measured and compared to measurements of commercial grade Gd. The samples have (x=0.86, y=1.08), (x=0.94, y=1.01) and (x=0.97, y=1.07) yielding Curie temperatures in the range 276–288 K. The magnetization, specific heat capacity and adiabatic temperature change have been measured over a broad temperature interval. Importantly, all measurements were corrected for demagnetization, allowing the data to be directly compared. In an internal field of 1 T the maximum specific entropy changes were 6.2, 5.1 and 5.0 J/kg K, the specific heat capacities were 910, 840 and 835 J/kg K and the adiabatic temperature changes were 2.3, 2.1 and 2.1 K for the three LaFeCoSi samples respectively. For Gd in an internal field of 1 T the maximum specific entropy change was 3.1 J/kg K, the specific heat capacity was 340 J/kg K and the adiabatic temperature change was 3.3 K. The adiabatic temperature change was also calculated from the measured values of the specific heat capacity and specific magnetization and compared to the directly measured values. In general an excellent agreement was seen.
Journal: Journal of Magnetism and Magnetic Materials - Volume 322, Issue 24, December 2010, Pages 3882–3888