Evolution of magnetic order in mechanically alloyed Al-1Â at%Fe

The evolution of ferromagnetic order in high-energy ball-milled Al-1 at% Fe before the onset of a considerable Fe-Al solid solution phase has been investigated using 57Fe Mössbauer and bulk magnetization studies. The unmilled sample does not exhibit bulk magnetic properties and an onset of bulk magnetization is observed only after 30 min of milling, when the grain size becomes comparable to the ferromagnetic exchange length. The Curie temperatures of all the samples are less than that of pure iron. The reduction in grain size is accompanied by an increase in coercivity and reduced remanence and a decrease in TC. The effective magnetic moment per iron atom decreases with the development of a non-magnetic, Al-rich Fe-Al solution on longer milling. The clustering of Fe at grain boundaries is responsible for the observed bulk magnetic ordering. The systematic variation of the magnetic properties has been qualitatively correlated with the evolution of microstructure, reduction in grain size and enhanced inter-granular exchange coupling.