A new Co–Fe-based ferromagnetic bulk metallic glass (BMG) was synthesized by copper mould casting method. The thermal stability and crystallization processes were investigated by differential scanning calorimetry (DSC) and X-ray diffraction (XRD). The soft magnetic behavior was studied by DC magnetic measurements. The high glass formation ability was interpreted in terms of the effective suppression of nucleation and growth of the intermetallic compounds which appear in the multicomponent system during solidification. The high thermal stability indicates that the new Co–Fe-based BMG could be used as high-temperature magnetic material. The low coercivity which was as low as 8 A/m for the as-cast sample was found in the Co–Fe-based metallic glass cylinder with a diameter of 1.5 mm.
Journal: Journal of Magnetism and Magnetic Materials - Volume 299, Issue 2, April 2006, Pages 492–495