Structural, magnetic and Mössbauer spectral studies of nanosize aluminum substituted nickel zinc ferrites

Nanosize aluminum substituted nickel zinc ferrites were prepared through aerosol route and characterized using TEM, XRD, magnetic measurements and Mössbauer spectroscopy. The particle size of as obtained samples was found to be ∼10 nm which increases up to ∼85 nm upon annealing at 1200 °C. The unit cell parameter ‘a’ decreases linearly with concentration of aluminum due to the small ionic radius of aluminum. The saturation magnetization for all the samples after annealing at 1200 °C lies in the range 12.9–72.6 emu/g and decreases linearly with concentration of aluminum. Room temperature Mössbauer spectra of all as obtained samples of ferrite compositions exhibited a broad doublet suggesting super paramagnetic nature. This doublet is further resolved into two doublets and assigned to the surface region and internal region atoms of the particles. The samples annealed at 1200 °C show broad sextets, which were fitted with five sextets, indicating different local environment of both tetrahedrally and octahedrally coordinated Fe cation.