Improvement in performance of a direct ethanol fuel cell: Effect of sulfuric acid and Ni-mesh

A direct ethanol fuel cell (DEFC) is developed with low catalyst loading at anode and cathode compared to that reported in the literature. Pt/Ru (40%:20% by wt.)/C and Pt-black were used as anode and cathode catalyst with loadings in the range of 0.5–1.2 mg/cm2. The temperatures of anode and cathode were varied from 34 °C to 110 °C, and the pressure was maintained at 1 bar. Although low catalyst loading was used, the cell performance is enhanced by 40–50% with the use of low concentration of sulfuric acid in ethanol and Ni-mesh as current collector at the anode. The power density 15 mW/cm2 at 32 mA/cm2 of current density is obtained from the single cell with 0.5 mg/cm2 loading of Pt–Ru/C at anode (90 °C) and Pt-black at cathode (110 °C). The performance of DEFC increases with the increase in ethanol and sulfuric acid concentrations, electrocatalyst loadings up to 1 mg cm−2 at anode and cathode. However, the performance of DEFC decreases with further increase in electrocatalyst loading.