Commercial LiCoO2 has been modified with MnSiO4 as a novel coating material. The structures, morphologies, overcharge behaviors and thermal stabilities of the pristine and MnSiO4-coated LiCoO2 materials were studied. The MnSiO4-coated LiCoO2 had initial discharge specific capacities of 181.1 and 232.2 mAh g−1 within the potential ranges 2.75–4.5 and 2.75–4.7 V (vs. Li+/Li), respectively. It was found that the overcharge tolerance of the coated cathode was significantly better than that of the pristine LiCoO2 under the same conditions – the discharge specific capacities of the coated cathode at upper charge cutoff voltages of 4.5 and 4.7 V were as high as 168.7 and 154.3 mAh g−1, respectively, after 50 cycles. Moreover, DSC showed that the coated LiCoO2 had a higher thermal stability than the pristine LiCoO2.
Journal: Electrochemistry Communications - Volume 10, Issue 8, August 2008, Pages 1136–1139