Development of Long REBCO with BMO Coated Conductors by PLD Method with High Production Rate

We have been developing long REBa2Cu3O7-δ (RE: Y, Gd and Eu etc.) with BaMO3 (M: Zr, Sn and Hf etc.) coated conductors by the combination of the ion-beam assisted deposition (IBAD) and the pulsed laser deposition (PLD) methods. REBa2Cu3O7-δ with BaMO3 coated conductors showed high in-field performance, therefore, these coated conductors could be expected for the industrial and commercial applications at high temperatures in magnetic fields. However, to realize the low production cost for long REBa2Cu3O7-δ with BaMO3 coated conductors, improvement of the production rate of the REBa2Cu3O7-δ layers containing BaMO3 rods with maintaining high superconducting properties is required. To solve these problems, we have tried deposition of the REBa2Cu3O7-δ layers with high superconducting properties by the PLD method with high production rate. As a result, we have successfully fabricated EuBa2Cu3O7-δ layers containing BaHfO3 rods with high in-field Jc and Ic by the PLD method with high production rate. This EuBa2Cu3O7-δ with BaHfO3 coated conductor exhibit a high Ic value of 412 and 48.7 A/cm-width at 77 K in self-field and 3 T, respectively at the deposition rate of about 40 μm/h and the production rate of 10 m/h for a 1.35 μm EuBCO layer thick.