Further study on the influence of thermal treatments on the glow curve structure in LiF:Mg,Cu,P (GR-200A)

• The influence of various annealing treatments on LiF:Mg,Cu,P glow-curve was investigated.
• For annealing temperatures above 240 °C the glow curves of LiF:Mg,Cu,P changed remarkably.
• The re-annealing influenced both the intensity and the peak shape at certain degree.
• The effect of re-annealing on the glow curve depends markedly on the annealing temperatures.

The influence of various annealing treatments with heating temperatures (TA) from 240 to 700 °C, with re-annealing at 240 °C, and with a combined re-annealing procedure of 20 min at 270 °C followed by 10 min at 240 °C on LiF:Mg,Cu,P (GR-200A) was investigated. As the TA increased, the intensity decreased rapidly to almost no signal at 340–380 °C then increased clearly and achieved a maximum at 540 °C. The position of the maximum intensity of the glow curve shifted basically in the direction of higher temperatures with an increase at TA and achieved a maximum of 279 °C when annealed at 460 °C. The re-annealing influenced both the intensity and the glow curve structure at certain degree. The effect of re-annealing on the glow curve depended markedly on the TA. With re-annealing at 240 °C, the intensity decreased as TA increased up to 360 °C then increased and achieved a maximum at 540 °C. The intensity could be restored fully when annealed at above 500 °C, however, the glow curve couldn't be restored fully. With a combined annealing, the shape of glow curve of a sample annealed at above 540 °C or below 320 °C was similar to that of the standard glow curve of LiF:Mg,Cu,P and the intensity and glow curve could be restored completely when annealed in the range 620–660 °C. It seems that the main roles of the re-annealing at 240 °C are to restore partially the intensity of peak 4 and peak shape for LiF:Mg,Cu,P when annealed at above 260 °C, and restore fully the total TL intensity of LiF:Mg,Cu,P when annealed at above 500 °C and the main roles of the combined re-annealing are to reduce the intensity of peak 5 and the total TL intensity, increase the intensity of peak 4 and restore the glow curve shape.