Facile synthesis of SAPO-34 with small crystal size for conversion of methanol to olefins

• SAPO-34 with small crystal was synthesized by dry gel liquid-phase transport method.
• The adding of TEAOH is favorable to form small crystals of SAPO-34.
• The SAPO-34 catalyst exhibits outstanding catalytic performance in MTO process.

SAPO-34 molecular sieves were fabricated by a dry gel liquid-phase transport method using morpholine (Mor) or morpholine–tetraethylammonium hydroxide (Mor–TEAOH) as the structure-directing agent (SDA). The prepared samples were characterized by scanning electron microscope (SEM), nitrogen adsorption–desorption, X-ray diffraction (XRD), ammonia temperature-programmed desorption (NH3-TPD), thermo-gravimetric analysis (TG) and Fourier transform infrared spectroscopy (FT-IR). The results indicated that the dry gel liquid-phase transport method is very effective to fabricate SAPO-34 molecular sieves with average crystal size about 0.6 μm using Mor–TEAOH as SDA and 3 μm using Mor as SDA, respectively. Moreover, the addition of TEAOH is beneficial to produce SAPO-34 with small crystal size. Methanol-to-olefins (MTO) reaction was chosen to test the catalytic performance of as-prepared SAPO-34 catalysts. The prepared SAPO-34 catalyst using Mor–TEAOH as SDA exhibited the excellent catalytic performance in MTO process owing to its small crystal size and high crystallinity. The conversion of methanol and selectivity of ethylene and propylene are up to 100% and 87.9%, respectively.

SAPO-34 with small crystal size of about 0.6 μm was fabricated by dry gel liquid-phase transport method. Methanol-to-olefins (MTO) reaction was chosen to test the catalytic performance of as-prepared SAPO-34 catalyst, indicating that the SAPO-34 catalyst exhibited the outstanding catalytic performance in MTO process.Figure optionsDownload as PowerPoint slide