Degradation mechanisms of pcBN tool material during Friction Stir Welding of Ni-base alloy 625

Tool wear is mainly caused by detachment of BN grains due to thermal softening of the metallic binder phase and dissolution of BN in the hot material in the stirred zone. Using low rotational speeds resulting in lower process temperatures reduces tool wear and results in a homogeneous stirred zone.