A-site cationic disorder induced significantly large magnetoresistance in polycrystalline La0.2Gd0.5Ba0.3MnO3 compound

The observation of significantly large magnetoresistance at the liquid nitrogen temperature range in the polycrystalline La0.2Gd0.5Ba0.3MnO3 (LGBMO) compound has been addressed in the present manuscript. The motivation of considering LGBMO sample is the average 'A' site ionic radius 〈rA〉 and tolerance factor (t), almost same as that of La0.7Sr0.3MnO3 (LSMO), which is a well studied colossal magnetoresistive material. Magnetoresistance of the LGBMO compound has been compared with the LSMO as well as parent compound La0.7Ba0.3MnO3(LBMO) to show the enhancement of magnetoresistance in LGBMO compound. This observed nature has been elucidated considering the disorder induced short range magnetic interaction due to the enhance size disorder parameter (σ2). Our study revels that, size disorder parameter plays the crucial role for enhancing the colossal magnetoresistance.