Structural, magnetic, and dielectric properties of multiferroic Co1−xMgxCr2O4 nanoparticles

We examined the structural, magnetic, and dielectric properties of Co1−xMgxCr2O4 nanoparticles with composition x = 0, 0.2, 0.4, 0.5, 0.6, 0.8 and 1 in detail. X-ray diffraction (XRD) revealed normal spinel structure for all the samples. Rietveld refinement fitting results of the XRD showed no impurity phases which signifies the formation of single phase Co1−xMgxCr2O4 nanoparticles. The average crystallite size showed a peak behaviour with maxima at x = 0.6. Raman and Fourier transform infrared (FTIR) spectroscopy also confirmed the formation of single phase normal spinel for all the samples and exhibited dominant vibrational changes for x ≥ 0.6. For x = 0 (CoCr2O4), zero field cooled/field cooled (ZFC/FC) magnetization curves showed paramagnetic (PM) to ferrimagnetic (FiM) transition at Tc = 97 K and a conical spiral magnetic order at Ts = 30 K. The end members CoCr2O4 (x = 0) and MgCr2O4 (x = 1) are FiM and antiferromagnetic (AFM), respectively. Tc and Ts showed decreasing trend with increasing x, followed by an additional AFM transition at TN = 15 K for x = 0.6. The system finally stabilized and changed to highly frustrated AFM structure at x = 1 due to formation of pure MgCr2O4. High field FC curves (5T) depicted nearly no effect on spiral magnetic state, which is attributed to strong exchange B-B magnetic interactions at low temperatures. Dielectric parameters showed a non-monotonous behaviour with Mg concentration and were explained with the help of Maxwell-Wagner model and Koop's theory. Dielectric properties were improved for nanoparticles with x = 0.6 and is attributed to their larger average crystallite size. In summary, Mg doping has significantly affects the structural, magnetic, and dielectric properties of CoCr2O4 nanoparticles, which can be attributed to variations in local magnetic exchange interactions and variation in average crystallite size of these chromite nanoparticles.