Development of Z-type hexaferrites for high frequency EMI shielding applications
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
فیزیک و نجوم
فیزیک ماده چگال
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Barium Z-type hexaferrites (Ba3Co2Cr2xFe24â2xO41 with x = 0, 0.3, 0.6 and 0.9) were synthesised using solid state reaction technique. X-ray diffraction (XRD) analysis confirmed the formation of single phase Z-type hexaferrite structure. From transmission electron microscopy (TEM) analysis platelet morphologies were observed in all the studied samples and the average grain size were calculated, which were around 100 nm. Magnetisation measurements (M-H) and (M-T) were carried out using vibrating sample magnetometer (VSM). Saturation magnetisation (Ms) was found to decrease with increasing Cr content in the samples whereas, magnetic coercive field (Hc) and remanent magnetisation (Mr) were increased. Electromagnetic absorption properties of all the ferrite samples were tested in 2-18 GHz frequency range using Agilent Vector Network Analyser. The sample Ba3Co2Cr1.2Fe22.8O41 (x = 0.6) had exhibited maximum microwave absorption of 99.8% at 5.34 GHz. All the samples showed broad absorption bandwidth of 3-3.2 GHz as well significantly high enough reflection loss of â10 dB. Therefore, the developed Z-type hexaferrites can be used for good electromagnetic shielding/absorber applications.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Magnetism and Magnetic Materials - Volume 441, 1 November 2017, Pages 303-309
Journal: Journal of Magnetism and Magnetic Materials - Volume 441, 1 November 2017, Pages 303-309
نویسندگان
S.B.S. Magham, M. Sharma, S.R. Shannigrahi, Hui Ru Tan, V. Sharma, Yu Song Meng, S. Idapalpati, R.V. Ramanujan, D.V.M. Repaka,