Preparation of hollow microspheres of Ce3+ doped NiCo ferrite with high microwave absorbing performance
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
فیزیک و نجوم
فیزیک ماده چگال
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Hollow microspheres of Ce3+ doped NiCo-ferrites were synthesized by template-based-deposition and surface reaction method with carbon sphere as the template. The phase structure, morphology, magnetic properties and wave absorbing properties of the sample were characterized by X-ray powder diffraction(XRD), Scanning electronic microscopy(SEM), Vibration sample magnetometer (VSM) and a network vector analyzer (NVA), respectively. The results indicated that the particle size of the carbon sphere sample prepared by hydrothermal method was about 0.5 µm and the particle size of the Ni0.5Co0.5Fe2O4 sample prepared by template-based method was about 300 nm. The influence of the amount of rare earth element on the magnetic and absorbing properties of sample was studied. The saturation magnetization and coercivity decreased gradually with the increase of the content of Ce. When the content of Ce was 0.02, the maximal saturation magnetization value and coercivity was 75.72 emu
- gâ1 and 789.88Â Oe, respectively. The associated ferrite hollow spheres have good absorbing performance, and the return loss value was â18.8Â dB at 5500Â MHz.
- gâ1 and 789.88Â Oe, respectively. The associated ferrite hollow spheres have good absorbing performance, and the return loss value was â18.8Â dB at 5500Â MHz.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Magnetism and Magnetic Materials - Volume 424, 15 February 2017, Pages 467-471
Journal: Journal of Magnetism and Magnetic Materials - Volume 424, 15 February 2017, Pages 467-471
نویسندگان
Hong-zhen Duan, Fang-ling Zhou, Xia Cheng, Guo-hong Chen, Qiao-ling Li,