Colloidal stability of iron oxide nanoparticles with multivalent polymer surfactants

• A new approach for making magnetic particles by polyelectrolyte surfactants.
• The particle distribution depends on the hydrophobicity of the polyelectrolyte.
• Polyelectrolyte with a negatively charge gives long-term stability of the particle.

This paper introduces a new approach for preparing magnetic colloidal suspensions with electrostatic repulsion between particles and polyelectrolyte surfactants. The surface charge of the iron oxide particles was positive in acidic aqueous conditions; however the surface charge of the colloid was negative in basic aqueous conditions due to the amphoteric property of Fe2O3. The long-term colloidal stability and particle distribution of the multivalent charged polymers, Poly(4-vinylbenzenesulfonate sodium salt) (PSS), Poly(acrylic acid) (PAA), and Poly(allylamine hydrochloride) (PAH) were compared with the monovalent surfactant sodium dodecyl sulfate (SDS). Both mono- and multivalent surfactant molecules showed good colloidal stability for extended periods of time. However, the particle distribution was dependent on the hydrophobicity of the surfactants’ functional groups. Polyelectrolytes with a negatively charged functional group showed good long-term stability of particles and a narrow particle distribution regardless of the acid dissociation constant (pKa) of the polymer.

Figure optionsDownload high-quality image (88 K)Download as PowerPoint slide