Spray-coating of superhydrophobic aluminum alloys with enhanced mechanical robustness

• We prepared a robust superhydrophobic surface on etched aluminum alloy by spray coating.
• The coating solution consisted of hydrophobic nanoparticles and precursor.
• Micro-protrusions on the etched aluminum alloy enhanced the coating mechanical robustness.
• Superhydrophobicity could be restored by a re-application of the spray coating solution.

A superhydrophobic aluminum alloy was prepared by one-step spray coating of an alcohol solution consisting of hydrophobic silica nanoparticles (15–40 nm) and methyl silicate precursor on etched aluminum alloy with pitted morphology. The as-sprayed metal surface showed a water contact angle of 155° and a roll-off angle of 4°. The coating was subjected to repeated mechanical tests, including high-pressure water jetting, sand particles impacting, and sandpaper shear abrasion. It remained superhydrophobic with a roll-off angle <10° up to three cycles of water jetting (25 kPa for 10 min) and sand particle impinging. After five cycles, the roll-off angle increased, but no more than 19° while the water contact angle remained greater than 150°. The superhydrophobic state was also maintained after three cycles of sandpaper abrasion. It was found that the micro-protrusion structures on the etched aluminum alloy played an important role to enhance the coating mechanical robustness, where the nanoparticles could grab on the rough surface, specifically in the groove structures, in comparison with the smooth glass substrates spray coated with the same materials. Further, we showed that the superhydrophobicity could be restored by spray a new cycle of the nanocomposite solution on the damaged surface.

Figure optionsDownload high-quality image (95 K)Download as PowerPoint slide