![عکس صفحه اول مقاله: Mesoporous aluminosilicates assembled from dissolved LTA zeolite and triblock copolymer in the presence of tetramethylammonium hydroxide Mesoporous aluminosilicates assembled from dissolved LTA zeolite and triblock copolymer in the presence of tetramethylammonium hydroxide](/preview/png/610391.png)
Zeolite Na-A crystals dissolved in a HCl solution were used as a single-source of silicon and aluminum for the synthesis of mesoporous aluminosilicates via a template-assisted method with an organic base tetramethylammonium hydroxide (TMAOH). Amphiphilic triblock copolymer Pluronic F127 (EO106PO70EO106) was used as template. Increasing the amount of TMAOH in the synthetic solution resulted in an increase in the aluminum content of the products. On the other hand, mesostructural periodicity was deteriorated with higher content of aluminum incorporated into the mesoporous framework. The samples with low Si/Al ratios less than 5 have wormhole-like pore structure, while the samples with Si/Al ratios more than 7 possess highly ordered mesoporous structure, a body-centered Im3mIm3m symmetry, with single crystal like morphology. The samples with Si/Al ratio of 7, which prepared at TMAOH molar concentration of 25 mM in the templating solution, possess BET surface area of 470 m2/g, pore size of 6.4 nm, and pore volume of 0.56 cm3/g. Aluminum atoms have successfully been incorporated in a tetra-coordinated position and remained stable even after calcination at 600 °C.
Zeolite Na-A crystals dissolved in a HCl solution were used as a single-source of silicon and aluminum for the synthesis of mesoporous aluminosilicates with body-centered Im3mIm3m symmetry via a copolymer-assisted method with an organic base tetramethylammonium hydroxide.Figure optionsDownload as PowerPoint slide
Journal: Journal of Colloid and Interface Science - Volume 333, Issue 2, 15 May 2009, Pages 491–496