Photoconductive oxotitanium phthalocyanine (TiOPc) nanoparticles with an average diameter of 3.6 nm were successfully prepared. These nanoparticles could be well dispersed in organic solvents such as 1,2-dichloroethane to form a stable organic sol of solvent-stabilized TiOPc nanoparticles. An obvious size effect of TiOPc semiconductor was revealed by the UV–vis absorption spectroscopy measurements. Single-layered photoreceptors were prepared by coating colloidal solutions containing the C2H4Cl2-stabilized TiOPc nanoparticles and a polycarbonate (PC) resin onto aluminum plates. Optimum xerographic properties of the present photoreceptors were obtained on a photoreceptor containing 20 wt% of the TiOPc nanoparticles, which exhibited a photoconductive sensitivity (E1/2E1/2) of 0.54 μJ/cm2 and could be positively charged to 596 V.
Photoconductive TiOPc nanoparticles with an average diameter of 3.6 nm were prepared and dispersed in polycarbonate films to fabricate single-layered photoreceptors with excellent xerographic properties in the positively charged model.Figure optionsDownload as PowerPoint slide
Journal: Journal of Colloid and Interface Science - Volume 325, Issue 1, 1 September 2008, Pages 198–202