Porous TiO2/SiO2 composite prepared using PEG as template direction reagent with assistance of supercritical CO2
موضوعات مرتبط
مهندسی و علوم پایه مهندسی شیمی شیمی کلوئیدی و سطحی
پیش نمایش صفحه اول مقاله
Porous TiO2/SiO2 composite prepared using PEG as template direction reagent with assistance of supercritical CO2
چکیده انگلیسی

Titania–silica mesoporous composites have been prepared using polyethylene glycol (PEG) 20,000 as a template direction reagent with the assistance of supercritical carbon dioxide (SC CO2). For this preparation method, the composite precursors of tetrabutyl titanate (TBTT) and tetraethyl orthosilicate (TEOS) were dissolved in supercritical CO2 and impregnated into PEG 20,000 using SC CO2 as swelling agent and carrier. After removal of the PEG template by calcination in air at suitable temperatures, porous titania–silica composites were obtained. Effects of CO2 pressure and temperature have been studied on the impregnation ratio during the supercritical fluid condition. The composite products were characterized by thermogravimetric analysis (TGA), X-ray diffraction (XRD), FTIR spectroscopy, nitrogen sorption–desorption experiments, scanning electronic microscope (SEM), and transmission electron microscope (TEM). XRD and nitrogen sorption–desorption experimental results indicate that the titania–silica composite crystallized in anatase phase and has a preferable BET surface area up to 301.98 m2/g. It was also demonstrated that the microstructure and macroproperty of TiO2/SiO2 composites depend strongly on the experimental pressure during the impregnation process in SC CO2. At suitable CO2 pressure, silica even can be found in a single crystalline structure in nature by observation of TEM. At the same time, SEM indicates that the composite product existed in a spheric form or a cubic form inserted with many holes. So this work provides a new route to control and obtain the special micrography of TiO2/SiO2 composites with the aid of suitable polymer templates in supercritical CO2.

Figure optionsDownload as PowerPoint slide

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Colloid and Interface Science - Volume 316, Issue 2, 15 December 2007, Pages 596–603
نویسندگان
, , ,