A simple route utilizing surfactant-assisted templating sol–gel process for synthesis of mesoporous Dy2O3 nanocrystal

A simple route of combined sol–gel process with surfactant-assisted templating technique was successfully employed for the first time to synthesize nanocrystalline mesoporous Dy2O3 with narrow monomodal pore size distribution under mild conditions. The nanocrystalline Dy2O3 with monomodal mesoporous characteristic was ultimately achieved by controlling the hydrolysis and condensation steps of dysprosium n-butoxide modified with acetylacetone in the presence of laurylamine hydrochloride surfactant aqueous solution. The synthesized material was methodically characterized by thermogravimetry and differential thermal analysis (TG-DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), selected-area electron diffraction (SAED), N2 adsorption–desorption, Brunauer–Emmett–Teller (BET) surface area analysis, and Barrett–Joyner–Halenda (BJH) pore size distribution analysis. The particle size of the synthesized Dy2O3 in nanosized range obtained from the SEM and HRTEM micrographs was in good accordance with the crystallite size estimated from the XRD result. The N2 adsorption–desorption result exhibited hysteresis pattern with single loop, indicating the existence of monomodal mesopore. The extremely narrow pore size distribution with mean pore diameter in the mesopore region of the synthesized Dy2O3 was also confirmed by the BJH result.

A simple route of surfactant-assisted templating sol–gel process was successfully utilized to synthesize nanocrystalline monomodal mesoporous Dy2O3. N2 adsorption–desorption analysis of the synthesized Dy2O3 exhibited IUPAC type IV pattern with hysteresis loop indicating the presence of prevalent mesopore, and pore size distribution was also extremely narrow and monomodal.Figure optionsDownload as PowerPoint slide