Simulation of abrasion to WC/Co hardmetals using a micro-tribology test system

In line with previous observations, it was found that the mechanisms of damage that occurred were removal of the cobalt from the binder phase region of the sample, cracking of the WC grains and re-embedment of WC fragments into remaining binder phase.