Influence of graphite content on the dry sliding and oil impregnated sliding wear behavior of Al 2024-graphite composites produced by in situ powder metallurgy method

The influence of graphite content on the dry sliding and oil impregnated sliding wear characteristics of sintered aluminum 2024 alloy-graphite (Al/Gr) composite materials has been assessed using a pin-on-disc wear test. The composites with 5-20 wt.% flake graphite particles were processed by in situ powder metallurgy technique. For comparison, compacts of the base alloy were made under the same consolidation processing applied for Al/Gr composites. The hardness of the sintered materials was measured using Brinell hardness tester and their bending strength was measured by three-point bending tests. Scanning electron microscopy (SEM) was used to analyze the debris, wear surfaces and fracture surfaces of samples. It was found that an increase in graphite content reduced the coefficient of friction for both dry and oil impregnated sliding, but this effect was more pronounced in dry sliding. Hardness and fracture toughness of composites decreased with increasing graphite content. In dry sliding, a marked transition from mild to severe wear was identified for the base alloy and composites. The transition load increased with graphite content due to the increased amount of released graphite detected on the wear surfaces. The wear rates for both dry and oil impregnated sliding were dependent upon graphite content in the alloy. In both cases, Al/Gr composites containing 5 wt.% graphite exhibited superior wear properties over the base alloy, whereas at higher graphite addition levels a complete reversal in the wear behavior was observed. The wear rate of the oil impregnated Al/Gr composites containing 10 wt.% or more graphite particles were higher than that of the base alloy. These observations were rationalized in terms of the graphite content in the Al/Gr composites which resulted in the variations of the mechanical properties together with formation and retention of the solid lubricating film on the dry and/or oil impregnated sliding surfaces.