Hip-simulator wear studies of an alumina-matrix composite (AMC) ceramic compared to retrieval studies of AMC balls with 1-7 years follow-up
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
شیمی کلوئیدی و سطحی
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
All balls and cups revealed stripe wear within 0.1Mc duration. Stripes expanded over 5Mc duration to span a 45-90° arc on the balls and covered an area of 150-350 mm2. The narrow wear scar on cup rims expanded circumferentially and radially with duration. The AMC/AMC performance represented a 5-12-fold wear reduction compared to controls; hybrid ALX/AMC combinations showed a 3-fold reduction. Tetragonal to monoclinic transformation was detected in all AMC bearings and peaked at less than 30% by end of study. In non-wear zones, monoclinic content averaged less than 20%. SEM and roughness mapping at 5Mc showed that AMC surfaces had superior resistance to stripe wear. The stripe wear and monoclinic transformations in the two retrieved AMC balls with alumina liners (3-7 years use) appeared similar to the laboratory study. Thus the monoclinic transformation was anticipated by the laboratory performance. It is therefore hypothesized that once the concentration of monoclinic reaches a certain level, further zirconia transformation is suppressed until the compressive alumina constraint can be overcome by additional wear. This appears to be a very different process compared to that seen with the yittria-stabilized zirconia balls used from year 1985.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Wear - Volume 267, Issues 5â8, 15 June 2009, Pages 702-709
Journal: Wear - Volume 267, Issues 5â8, 15 June 2009, Pages 702-709
نویسندگان
I.C. Clarke, D.D. Green, P.A. Williams, K. Kubo, G. Pezzotti, A. Lombardi, A. Turnbull, T.K. Donaldson,