High-temperature tribological properties of a cathodic arc ion-plated (V,Ti)N coating
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
شیمی کلوئیدی و سطحی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: High-temperature tribological properties of a cathodic arc ion-plated (V,Ti)N coating High-temperature tribological properties of a cathodic arc ion-plated (V,Ti)N coating](/preview/png/620033.png)
چکیده انگلیسی
The high-temperature tribological properties of a cathodic arc ion-plated (V,Ti)N coating have been investigated with a SRV high-temperature friction and wear tester. After heating in air at temperatures above 500 °C, V2O5 and TiO2 phases were identified on surfaces of (V,Ti)N coating with V2O5-type platelets as the major oxidized product. (V,Ti)N coatings exhibit a friction coefficient in the range of 0.53-1.08 and a wear rate in the range of 1.69 Ã 10â7-1.31 Ã 10â5 mm3/Nm, depending on test temperature used. At low temperatures, the presence of oxide debris induced by tribological stressing on the load-bearing regions reduces direct contact between (V,Ti)N coating and Al2O3, and generates a mild wear, however, adherent and compacted wear-protective oxide layers are not developed. At temperature of 500 °C or above, the wear-protective oxide layers containing thermally-oxidized V2O5 platelets deform plastically to produce a lubricious and smooth appearance to reduce friction. Raman spectroscopy was used to identify the structures of wear debris and coating surfaces after wear tests. Tribochemical reactions are the dominating wear phenomena at low temperatures. The wear debris generated during the wear process consists mainly of the V2O5-type tribo-oxides.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Wear - Volume 263, Issues 7â12, 10 September 2007, Pages 1347-1353
Journal: Wear - Volume 263, Issues 7â12, 10 September 2007, Pages 1347-1353
نویسندگان
J.H. Ouyang, T. Murakami, S. Sasaki,