- Nanocrystalline 8Â mol% YSZ synthesized via dendrimer precursor route.
- Surface area of YSZ powder is 37Â m2/g and crystallite size 8-10Â nm.
- 99.55% theoretical density realized by sintering at 1550 °C.
- The process has the potential for synthesis in pilot plant scale.
Polyamido amine dendrimer (PAMAM), synthesized from hexamethylene diamine and methyl methacrylate, was used to prepare nanocrystalline 8 mol% yttria stabilized zirconia (YSZ) powder. The nanocrystalline ceramic powder was characterized by XRF, XRD, TEM, SEM, particle size, surface area analyzer and ionic conductivity meter. The surface area of YSZ powder was 37 m2/g and crystallite size 8-10 nm. The green compact of YSZ powder was sintered at 1550 °C to 99.55% theoretical density (TD).
Sintered 8Â mol% YSZ synthesized via PAMAM dendrimer precursor route.43
Journal: Advanced Powder Technology - Volume 27, Issue 5, September 2016, Pages 1879-1884