![عکس صفحه اول مقاله: Correlation of shear flocculation of some salt-type minerals with their wettability parameter Correlation of shear flocculation of some salt-type minerals with their wettability parameter](/preview/png/688232.png)
This paper considers the importance of surface hydrophobicity in the shear flocculation process and presents a correlation between the shear flocculation and the wettability parameter for barite, celestite and calcite as salt-type minerals. The critical surface tension of wetting (γc) as a wettability parameter describes wetting characteristics of any mineral. The variation of the shear flocculation behaviours of barite, celestite and calcite with sodium oleate concentration in various methanol solutions was investigated. The shear flocculation of these minerals in the methanol solutions increased rapidly towards the optimum surfactant concentration, and thereafter remained relatively constant or increased slightly. On the other hand, the shear flocculation of the minerals decreased with increasing methanol concentration, depends on decreasing surface tension. The γc values of these minerals as a function of surfactant concentration were determined using a shear flocculation approach. It was found that the γc values did not change much at surfactant concentrations above the optimum. This result provides a reason for the observed lack of significant increase in the shear flocculation of the mineral suspensions when surfactant concentrations higher than the optimum are used. Furthermore, a strong correlation between the effective shear flocculation and the critical surface tension of wetting (γc) value was established. As the effective shear flocculation of these salt-type minerals increased sharply below a particular γc value, it was not much improved after reaching the γc value obtained at the optimum concentration of sodium oleate.
Journal: Chemical Engineering and Processing: Process Intensification - Volume 46, Issue 12, December 2007, Pages 1341–1348