Dependence of the friction durability of extremely thin diamond-like carbon films on film thickness
ترجمه فارسی عنوان
وابستگی دوام اصطکاکی فیلمهای کربنی الماس بسیار نازک بر ضخامت فیلم
موضوعات مرتبط
مهندسی و علوم پایه مهندسی شیمی شیمی کلوئیدی و سطحی
چکیده انگلیسی
Tribological durability properties of extremely thin diamond-like carbon (DLC) films (thickness 0.03-5 nm) deposited using filtered cathodic vacuum arc (FCVA) and plasma-chemical vapor deposition (P-CVD) methods were evaluated using load-increase-and-decrease, ball-on-disk, and low-load reciprocating friction tests. Friction durability notably increased at a certain film thickness for FCVA-DLC and P-CVD-DLC films. These thicknesses were nearly equal to surface roughness and corresponded to film thickness at which the nanowear profiles changed from protuberance to grooves and at which nanoscratch resistance increased. Excellent friction durability of FCVA-DLC films (thickness≥0.4 nm), evaluated by rapid increase in the friction coefficient, was observed. In contrast, the friction durability of P-CVD-DLC films gradually increased when the film thickness was 0.6 nm or greater. When the thickness of the DLC films was 2.0 nm or greater, the films did not exhibit a rapid increase in their friction coefficient within the total number of testing cycles. The tribological properties of extremely thin DLC films depend on film thickness; extremely thin FCVA-DLC films exhibit excellent wear resistance. The film thickness at which FCVA-DLC films endured the total number of test cycles was approximately one-fifth the corresponding thickness of CVD-DLC films, evaluated by the three different friction tests.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Wear - Volumes 356–357, 15 June 2016, Pages 66-76
نویسندگان
, , ,