Mapping wear mechanisms of TiC/Ti composite coatings
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
شیمی کلوئیدی و سطحی
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
In this work, a fundamental study of the wear transition regimes with respect to sliding speed and normal load was carried out for a pin-on-disk sliding couple, involving hardened steel (disks) and titanium base titanium carbide composite coatings (pins). The coating was deposited using a Tungsten Inert Gas (TIG) welding torch melting process. The sliding speed was varied from 0.38 to 1.5 m sâ1, and the normal load was varied from 10 to 50 N. Dry sliding wear behavior of the disks was characterized by abrasive-oxidative wear at lower normal loads while adhesive-oxidative wear predominated at higher loads with iron oxide transfer to the TiC composite coated pins. In contrast, micro-polishing and adhesive wear predominated the TiC composite coatings pins along with very mild abrasive wear in evidence. However, the wear regime depended on the conditions with a range of transitions observed over the sliding speeds and loads tested. Wear maps have been constructed to represent the wear mode transitions and the observed wear mechanisms have been discussed.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Wear - Volumes 328â329, 15 April 2015, Pages 498-508
Journal: Wear - Volumes 328â329, 15 April 2015, Pages 498-508
نویسندگان
G. Rasool, S. Mridha, M.M. Stack,