The reciprocating wear behaviour of TiC-304L stainless steel composites prepared by melt infiltration
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
شیمی کلوئیدی و سطحی
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
TiC-based ceramic-metal composites, or cermets, are widely used in applications requiring wear and corrosion resistance. In the present work, a family of novel TiC-stainless steel (grade 304L) cermets has been developed using vacuum melt infiltration (1500 °C/1 h), with steel binder contents varied from 5 to 30 vol%. Microstructural analysis showed a homogenous distribution of TiC within the steel binder, with mean TiC grain sizes of â¼6 μm. Increasing the steel content resulted in an increase in the indentation fracture resistance and a decrease in the hardness. The reciprocating wear resistance of the cermets was assessed using a ball-on-flat geometry, using a WC-Co sphere dry sliding on the polished cermet surface. It was shown that there is an increase in the specific wear rate with both increasing load and binder content. Similarly, a higher coefficient of friction was observed with higher steel binder contents. The morphology of the worn surface was investigated using scanning electron microscopy, and associated energy dispersive X-ray spectroscopy, to more fully understand the operative wear mechanisms. Evidence of a transition from two- to three-body abrasive wear was observed, together with the formation of a tribolayer, indicating that adhesive wear was also occurring.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Wear - Volume 303, Issues 1â2, 15 June 2013, Pages 321-333
Journal: Wear - Volume 303, Issues 1â2, 15 June 2013, Pages 321-333
نویسندگان
Chukwuma C. Onuoha, Georges J. Kipouros, Zoheir N. Farhat, Kevin P. Plucknett,