Morphology dependent amplified spontaneous emission in π-conjugated polymer

The amplified spontaneous emission (ASE) spectra of a π-conjugated polymer Poly [2-methoxy-5-(2′-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) are studied in as-cast film, annealed film, 1 mg/ml solution and 2.5 mg/ml solution, respectively, using a 10 ns pulsed laser as an excitation source. We found that for annealed film (420 K), the ASE is hardly achieved compared to the as-cast film, which is consistent with the formation of the aggregation; whereas the film's temperature had much less effect on its ASE threshold. In solution, the ASE spectra show both 0-0 peak and 0-1 peak in 1 mg/ml solution, but only 0-1 peak in 2.5 mg/ml one. When the temperature of solution increases slightly from 300 K to 330 K, the ASE threshold increases dramatically in 1 mg/ml solution but slightly in 2.5 mg/ml one. Our results show the important role the morphology played in the ASE spectra in both film and solution. Therefore, controlling the interchain interaction in PCPs may be the key factor for performance of the organic lasers.