Carbide and nitride precipitation during laser cladding of Inconel 718 alloy coatings

The microstructure of the laser clad Inconel 718 alloy coating was observed by scanning electron microscope (SEM). The chemical composition of precipitation phases was investigated by energy dispersive spectrometer (EDS) and solid phase microextraction (SPME). The crystal structure and lattice constants of precipitation are determined by transmission electron microscope (TEM). Vickers hardness of the coatings and the nanohardness of the interstitial phases were measured. The insular carbide (MC) and the tetragonal nitride (MN) with face-centered cubic (FCC) structure are rich in Ti and Nb but depleted in Ni, Fe and Cr due to the interdiffusion and redistribution of alloying elements between MC and MN and supersaturated matrix. MC and MN were precipitated in the forms of (Nb0.12Ti0.88)C1.5 and (Nb0.88Ti0.12)N1.5, and the Gibbs free energies of formation can be expressed as ΔG[(Nb0.12Ti0.88)C1.5]0=−122.654-3.1332T(kJ/mol) and ΔG[(Nb0.88Ti0.12)N1.5]0=−157.814-3.0251T(kJ/mol). The nanohardness and Young's modulus of the MC and MN were much higher than the matrix, and the plastic deformation energy of interstitial phases was lower than the matrix. The precipitation of MC and MN is beneficial to the mechanical properties of coating.