Probabilistic evaluation on fatigue crack growth behavior in nickel based GH4169 superalloy through experimental data
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی مکانیک
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Probabilistic evaluation on fatigue crack growth behavior in nickel based GH4169 superalloy through experimental data Probabilistic evaluation on fatigue crack growth behavior in nickel based GH4169 superalloy through experimental data](/preview/png/7168810.png)
چکیده انگلیسی
The present paper developed a stochastic model to evaluate the scatter in fatigue crack growth (FCG) behavior of turbine disc GH4169 superalloy. Model parameters were calculated based on systematic experiments on compact tension (CT) specimens cut from the rim and installation flange locations of a turbine disk at corresponding service temperatures with stress ratios of 0.1 and 0.5. Based on the experimental data, piecewise FASTRAN model combined with Dugdale strip-yield model that includes the crack closure effect in GH4169 superalloy were proposed to formulate the deterministic FCG model. The probabilistic distribution of FCG rate was represented by a life distribution factor (LDF), combined with the deterministic model. Modeling results revealed that the variance of FCG rate followed a decrease-to-increase trend as crack propagates, which was consistent with the microstructural dependence of FCG revealed in typical polycrystalline materials. Proposed probabilistic model effectively reflected the stochastic property of FCG, offering a promising tool for probabilistic damage tolerance assessment (DTA).
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Engineering Fracture Mechanics - Volume 196, 1 June 2018, Pages 71-82
Journal: Engineering Fracture Mechanics - Volume 196, 1 June 2018, Pages 71-82
نویسندگان
Dianyin Hu, Jianxing Mao, Xiyuan Wang, Fanchao Meng, Jun Song, Rongqiao Wang,