Mixed-mode fracture of a superelastic NiTi alloy: Experimental and numerical investigations
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی مکانیک
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
The evolution of mixed-mode fracture in a superelastic NiTi (50.8â¯at.% Ni) was experimentally investigated by using a specific loading fixture. The NiTi alloy was fabricated using vacuum arc re-melting method and characterized by using differential scanning calorimetry, X-ray diffraction and tensile tests. Fracture tests were performed according to the ASTM standard E399. The butterfly-shaped specimens were used for conducting the mixed-mode fracture experiments and the fracture toughness parameters were obtained in the range of mode-I to mode-II by interchanging the loading angle from 0° to 90°. Also, in order to validate the fixture performance, the results in mode-I were compared with a standard compact tension (CT) specimen. Finite element implementation was carried out by using a user subroutine (UMAT) according to Boyd-Lagoudas phenomenological model and stress intensity factors were calculated by using well-known Linear Elastic Fracture Mechanics (LEFM) formulation. The results of mixed-mode fracture test revealed that the cracked specimen is tougher in mode-I loading compared with mode-II loading conditions. Finally, the fracture surfaces obtained at different mixed-mode loading conditions were investigated by using scanning electron microscopy (SEM) technique to gain a closer look into the failure mechanisms.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Engineering Fracture Mechanics - Volume 190, 1 March 2018, Pages 273-287
Journal: Engineering Fracture Mechanics - Volume 190, 1 March 2018, Pages 273-287
نویسندگان
B. Katanchi, N. Choupani, J. Khalil-Allafi, R. Tavangar, M. Baghani,