Effect of compound loading on microstructures and mechanical properties of 7075 aluminum alloy after severe thixoformation
ترجمه فارسی عنوان
اثر بارگذاری ترکیب بر روی ریزساختارها و خواص مکانیکی آلومینیوم 7075 پس از تکثیر شدید
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی صنعتی و تولید
چکیده انگلیسی
Solid-liquid segregation often occurred during thixoforming of wrought aluminum alloys, which can result in uneven structures and mechanical properties. In this work, a novel compound loading method was introduced in thixoforming 7075 aluminum alloys. The results show that the solid-liquid segregation can be alleviated evidently by compound loading, and the microstructures of periphery area were improved significantly. As the secondary loading displacement increased from 0Â mm to 5Â mm, the ultimate tensile strength (UTS) of the periphery area increased little (â¼510Â MPa), and the yield strength (YS) even decreased slightly from 486Â MPa to 470Â MPa. However, the elongation to fracture of the periphery area increased from 1.94% to 4.3% with increment of 122%. On the contrary, the compound loading has limited effect on the tensile mechanical properties of the center area. The tensile fracture surfaces exhibited typical brittle rupture in the periphery area, while the fracture surfaces of the center were dominated by a large number of dimples and tear ridges showing typical ductile fracture features. Compound loading is an effective method to homogenize the microstructures and mechanical properties of thixoformed wrought aluminum alloys.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Materials Processing Technology - Volume 229, March 2016, Pages 467-474
Journal: Journal of Materials Processing Technology - Volume 229, March 2016, Pages 467-474
نویسندگان
Gang Chen, Qiang Chen, Jin Qin, Zhi-ming Du,