Ultra-high-temperature tensile properties and fracture behavior of ZrB2-based ceramics in air above 1500 °C
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Nearly fully dense ZrB2-SiC-graphite composites were fabricated from commercially available powder at 1900 °C by hot pressing. The tensile strength of ZrB2-based ceramics was measured in air up to 1750 °C, which is the first reported tensile strength measurement in air above 1500 °C. A mechanical testing apparatus capable of testing material in ultra-high temperature under air atmosphere was built, evaluated, and used. Tensile strength was measured as a function of temperature up to 1750 °C in air. The respective average values of the tensile strength measured at 1550 °C, 1650 °C, and 1750 °C are 58.4, 44.8, and 21.8 MPa, which are 49.4%, 37.9%, and 18.4% of their room-temperature strength (118.2 MPa), respectively. Moreover, the tensile fracture behaviors and mechanism of ZrB2-based ceramics at different testing temperatures were discussed based on microstructure characterization.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials & Design (1980-2015) - Volume 52, December 2013, Pages 17-22
Journal: Materials & Design (1980-2015) - Volume 52, December 2013, Pages 17-22
نویسندگان
Rubing Zhang, Xiangmeng Cheng, Daining Fang, Liaoliang Ke, Yuesheng Wang,