Synthesis of Mg-Al and Zn-Al-layered double hydroxide nanocrystals using laser ablation in water

In this paper, we report our results on the synthesis of Mg-Al and Zn-Al-layered double hydroxides using the laser ablation in the liquid technique. To prepare these layered double hydroxides (LDH) we first began with the laser generation of a Mg (or zinc) target submerged in deionized water and then ablated an aluminum target submerged in the previously prepared Mg-deionized water suspensions (Mg-dw) to produce Mg-Al LDH and in Zn-dw to prepare Zn-Al LDH. In these ablation tests, the Mg ablation duration was selected to vary from 5 to 60 min, while the Al ablation duration was kept constant at 30 min for all samples. The generated Mg-Al LDH was a gel-like and well crystallized nanoparticles of a rod-like shape and were arranged in a well-organized pattern. When the Mg ablation duration between 25 and 35 min, the synthesized nanocrystals were stoichiometric with a formula of Mg6Al2(OH)184.5(H2O), the interlayer distance (d(0 0 3)-spacing) was 7.8 Å and the average grain size was 8.0 nm. The synthesized Zn-Al LDH revealed various lamellar thin plate-like nanostructures of hexagonal morphologies. The average diameters of these structures was about 500 nm and the thickness of a single layer was approximately about 6.0 nm. The XRD diffraction peaks were indexed in hexagonal lattice with ao=3.07 Å and co=15.12 Å. These indexes were (0 0 2), (0 0 4), and (0 0 8) and the corresponding interlayer distances, d-spacing (Å), were 7.56 (0 0 2), 3.782 (0 0 4), and 1.891 (0 0 8), respectively.